Search found 7 matches
- Fri Feb 18, 2011 11:16 am
- Forum: Silencersmithing Forum
- Topic: Form 1 can finished
- Replies: 16
- Views: 13518
Re: Form 1 can finished
I bought this tubing from Ebay and used it on a barrel that I turned down to 3/8" and built it back up by winding carbon fiber and epoxy. To cover my hand winding I used this tube then used the leftovers for the can. The tubing is filament wound at what looks like 45-55 degrees which is ideal f...
- Wed Feb 16, 2011 7:36 am
- Forum: Silencersmithing Forum
- Topic: Form 1 can finished
- Replies: 16
- Views: 13518
Re: Form 1 can finished
Weight : about 7 oz Length : 6" Dia : 1.060" Core and end cap material: 6al-v4 titanium Split tube material 304SS Outer tube material filament wound carbon fiber I have around 100 rounds thru it so far. In the picture above there was probably 20 rounds thru it. It seems quite but I want to...
- Wed Feb 16, 2011 6:42 am
- Forum: Silencersmithing Forum
- Topic: Form 1 can finished
- Replies: 16
- Views: 13518
Re: Form 1 can finished
SRM,
You wouldn’t believe how clean a hole a solid carbide bullet can punch.
You wouldn’t believe how clean a hole a solid carbide bullet can punch.
- Tue Feb 15, 2011 11:59 am
- Forum: Silencersmithing Forum
- Topic: Form 1 can finished
- Replies: 16
- Views: 13518
- Tue Feb 15, 2011 11:57 am
- Forum: Silencersmithing Forum
- Topic: Form 1 can finished
- Replies: 16
- Views: 13518
Form 1 can finished
Thanks for the help from everyone on this site.
- Sun Jan 02, 2011 6:26 am
- Forum: Silencersmithing Forum
- Topic: Monocore Mistake
- Replies: 13
- Views: 3805
Re: Monocore Mistake
The hole thru the part was left out because this was a test/setup piece. I plan on
drilling it before milling the baffle shapes.
drilling it before milling the baffle shapes.
- Thu Dec 30, 2010 5:47 am
- Forum: Silencersmithing Forum
- Topic: Monocore Mistake
- Replies: 13
- Views: 3805
Monocore Mistake
Made a mistake in programing a test piece.
What would this do?
What would this do?