Cleaning K-Baffles

Post by mcrump »

Has anyone ever tried cleaning their 7075 k baffles in a wet brass cartridge tumbler using those .047 stainless steel pins? Just curious.
Spectrum Tactical Solutions
FFL 01/SOT/07 license holder
Master Machinist
User avatar
RPM509
Senior Silent Operator
Posts: 145
Joined: Fri May 06, 2011 8:54 pm
Location: 66048

Re: Cleaning K-Baffles

Post by RPM509 »

I suspect it would work fine, and over a period of time slowly, ever so slowly, start to damage the baffles.
Aluminum baffles getting bombarded by stainless steel pins....
Pins made of a softer aluminum may be ideal.
"a butt tuba" - Palindrome
User avatar
CMV
Silent But Deadly
Posts: 757
Joined: Thu Feb 09, 2012 4:31 pm
Location: NC

Re: Cleaning K-Baffles

Post by CMV »

It doesn't' hurt cartridge brass which is also much softer than SS. The solution might be a problem - many people use the same solution for SS pin wet tumbling as you would for ultrasonic - a few drops of Dawn & LemiShine. Don't know how AL does in an acidic bath.
--------------------------------------

"Sorry but you cannot use search at this time. Please try again in a few minutes"
"This board is currently disabled"
These things make me :(
User avatar
RPM509
Senior Silent Operator
Posts: 145
Joined: Fri May 06, 2011 8:54 pm
Location: 66048

Re: Cleaning K-Baffles

Post by RPM509 »

Usually brass being cleaned in ss pins and solution only last X amount of reloads and then are tossed or recycled, usually before
any significant damage shows from it. SS pins can and will damage brass and aluminum over a period of time, acceptable on items that have a limited life expectancy, not for baffles.
"a butt tuba" - Palindrome
fastfire
Silent But Deadly
Posts: 185
Joined: Fri Mar 12, 2010 9:19 pm
Location: I-D-HO

Re: Cleaning K-Baffles

Post by fastfire »

RPM509 wrote:Usually brass being cleaned in ss pins and solution only last X amount of reloads and then are tossed or recycled, usually before
any significant damage shows from it. SS pins can and will damage brass and aluminum over a period of time, acceptable on items that have a limited life expectancy, not for baffles.
I have several hundred Lapua .223 brass that has more that 30 reloading's.
All these Lapua cases have been cleaned in a Tumbler's Tumbler using SS pins since they were new.
I anneal after each firing.
Never found any damage done from the SS pins.
Historian
Silent But Deadly
Posts: 3503
Joined: Mon Mar 29, 2010 10:37 pm

Re: Cleaning K-Baffles

Post by Historian »

Anyone place a K in a lathe collet and brush
with fine brass brush dipped in baking soda - wearing face mask?
User avatar
RPM509
Senior Silent Operator
Posts: 145
Joined: Fri May 06, 2011 8:54 pm
Location: 66048

Re: Cleaning K-Baffles

Post by RPM509 »

fastfire wrote:
RPM509 wrote:Usually brass being cleaned in ss pins and solution only last X amount of reloads and then are tossed or recycled, usually before
any significant damage shows from it. SS pins can and will damage brass and aluminum over a period of time, acceptable on items that have a limited life expectancy, not for baffles.
I have several hundred Lapua .223 brass that has more that 30 reloading's.
All these Lapua cases have been cleaned in a Tumbler's Tumbler using SS pins since they were new.
I anneal after each firing.
Never found any damage done from the SS pins.

Then you're not measuring very well.

It defies the laws of physics to state that amount of tumbling of brass cases, in stainless steel media, isn't doing any damage.
It might not be apparent to the naked eye, but I'd bet those walls are getting a tiny bit thinner.

Would you do the same with soft aluminum baffles? I wouldn't. At least not very many times or for extended periods.

30 reloads, even with annealing is an insane amount. All bolt-action, with high quality brass (Lapua is), and annealing after every firing, with minimal sizing
maybe 15-20 reloads, assuming low power at that. I would not trust brass, even it it didn't have any visible signs of stress or fracture showing with that many
reloads. :shock:
"a butt tuba" - Palindrome
fastfire
Silent But Deadly
Posts: 185
Joined: Fri Mar 12, 2010 9:19 pm
Location: I-D-HO

Re: Cleaning K-Baffles

Post by fastfire »

RPM509 wrote:
fastfire wrote:
RPM509 wrote:Usually brass being cleaned in ss pins and solution only last X amount of reloads and then are tossed or recycled, usually before
any significant damage shows from it. SS pins can and will damage brass and aluminum over a period of time, acceptable on items that have a limited life expectancy, not for baffles.
I have several hundred Lapua .223 brass that has more that 30 reloading's.
All these Lapua cases have been cleaned in a Tumbler's Tumbler using SS pins since they were new.
I anneal after each firing.
Never found any damage done from the SS pins.

Then you're not measuring very well.

It defies the laws of physics to state that amount of tumbling of brass cases, in stainless steel media, isn't doing any damage.
It might not be apparent to the naked eye, but I'd bet those walls are getting a tiny bit thinner.

Would you do the same with soft aluminum baffles? I wouldn't. At least not very many times or for extended periods.

30 reloads, even with annealing is an insane amount. All bolt-action, with high quality brass (Lapua is), and annealing after every firing, with minimal sizing
maybe 15-20 reloads, assuming low power at that. I would not trust brass, even it it didn't have any visible signs of stress or fracture showing with that many
reloads. :shock:

These all have been fired in the same AR15, NO BOLT GUN
User avatar
RPM509
Senior Silent Operator
Posts: 145
Joined: Fri May 06, 2011 8:54 pm
Location: 66048

Re: Cleaning K-Baffles

Post by RPM509 »

Next batch of new brass I pick up, will mark and measure with some micrometers and see what kind of wear after tumbling/reloading they experience. Curious now.
"a butt tuba" - Palindrome
vaeevictiss
Silent But Deadly
Posts: 172
Joined: Sat Sep 15, 2012 1:04 pm

Re: Cleaning K-Baffles

Post by vaeevictiss »

What i found works great for soft aluminum baffles is a blasting cabinet with walnut media. I have an SS tumbler i use for my brass but id never think of putting aluminum in there. I have however used it to clean the steel baffles in my Spectre and it does a phenomenal job.
User avatar
fishman
Silent But Deadly
Posts: 1444
Joined: Sun Dec 20, 2015 7:15 pm

Re: Cleaning K-Baffles

Post by fishman »

Brass shells and baffles are nothing alike. After you tumble brass you resize, shoot it, and fire form it. Any dimensional changes from tumbling will be taken care of by resizing dies and fire forming. Baffles don't get that luxury.

Is the deformation from tumbling aluminum in stainless steel going to be significant, or even noticeable? I have no clue. But don't compare brass tumbling to baffle tumbling so closely for those reasons.
300 blackout form 1: http://www.silencertalk.com/forum/viewtopic.php?f=10&t=137293

5.56 form 1:
http://www.silencertalk.com/forum/viewtopic.php?f=10&t=141800&p=955647#p955647
User avatar
RPM509
Senior Silent Operator
Posts: 145
Joined: Fri May 06, 2011 8:54 pm
Location: 66048

Re: Cleaning K-Baffles

Post by RPM509 »

fishman wrote:Brass shells and baffles are nothing alike. After you tumble brass you resize, shoot it, and fire form it. Any dimensional changes from tumbling will be taken care of by resizing dies and fire forming. Baffles don't get that luxury.

Is the deformation from tumbling aluminum in stainless steel going to be significant, or even noticeable? I have no clue. But don't compare brass tumbling to baffle tumbling so closely for those reasons.
Not talking about the outside dimension of the brass after sizing or fire-forming, rather it's thickness.
Simple science tells me that very thin layers are being ground away from the brass when tumbled in stainless media.
Mostly on the exterior, but also amounts of the interior, thinning the brass walls. Measurable? I suspect after many times yes.
To state that no material is being lost is patently false. Aluminum I am sure would lose much more, given everything being equal.
How long or many tumbles before it becomes an actual problem? I have no clue.
Still wouldn't tumble aluminum baffle in stainless media often, or for extended periods of time...unless I was an 02/SOT and could make my own
replacements willy-nilly that is.
"a butt tuba" - Palindrome
User avatar
fishman
Silent But Deadly
Posts: 1444
Joined: Sun Dec 20, 2015 7:15 pm

Re: Cleaning K-Baffles

Post by fishman »

I don't think material is going to be removed fast enough to matter. I do agree that minute amounts of material get removed during tumbling. However, I think surface finish changes are going to affect dimensions much more than material removal will. I have no data to back up this hypothesis.
300 blackout form 1: http://www.silencertalk.com/forum/viewtopic.php?f=10&t=137293

5.56 form 1:
http://www.silencertalk.com/forum/viewtopic.php?f=10&t=141800&p=955647#p955647
Tony M.
Silent But Deadly
Posts: 368
Joined: Wed Jul 31, 2013 11:42 pm
Location: FL

Re: Cleaning K-Baffles

Post by Tony M. »

RPM509 wrote:
Not talking about the outside dimension of the brass after sizing or fire-forming, rather it's thickness.
Simple science tells me that very thin layers are being ground away from the brass when tumbled in stainless media.
Actually, the SS pins are doing more to burnish the brass than to abrade it. With aluminum, being less ductile than the brass, I would be more concerned with edge deformation than material loss. I would also worry more about the baffles causing damage to one another than the pins doing damage. Tumbling one at a time would be a solution, but too slow for my taste.

Citric acid (lemishine) will eat the aluminum, and should not be used, neither should any other particularly acidic or caustic cleaning agents.

If the baffles are anodized, I would expect to see the finish degrade over time due to the burnishing process breaking up the hard surface layer.